STEP-PRO
Woven pad made
of cellulose triacetate
STEP-PRO pad is woven with strands of cellulose triacetate, a natural linear glucose polymer, giving it a silky appearance. The formation
of these exceptionally resistant microfibrils reinforces the hardness of the mesh constructed with the twisted and crossed weave of its
yarns. The fabric’s low moisture absorbency (5%) ensures high stock removal. It asserts the quality of sharp corners. The roughness is
very uniform without oversized machining marks. STEP-PRO is therefore indispensable for quality pre-polishing.
Highlights
Hard, even pad surface helps prepare for polishing operations
Keeps sharp angles
Above-average pad life
Recommended for long cycles
High abrasion rate (pre-polishing)
Excellent geometry
Product Specifications
Base material
Crisscross weave of cellulose acetate yarns; smooth satin top; hard pad
Shelf life
12 months
Applications
standard:
Ø 200 mm – Ø 400 mm
non-standard:
Ø 401 mm – Ø 1’300 mm
| Slurry additive | Base material | Hardness [Shore A] | Density [g/cm³] | Thickness [mm] |
|---|---|---|---|---|
| ALUPOL-PLUS | Viskose | 82 | 620 | 0,65 |
| MAMBO | Poromer | 65 | 814 | 1,50 |
| QUICK-STEP | Poromer | 97 | 528 | 0,50 |
| SAMBA-N | Polyacrylonitril | 87 | 840 | 1,50 |
| STEP-PLUS | Cellulose acetate | 96 | 720 | 0,65 |
| STEP-PRO | Cellulose triacetate | 96 | 660 | 0.85 |
| SWING-PLUS | Viscose fiibers | 88 | 660 | 0.85 |
Interested in our
STEP-PRO Polishing Pad?
We are happy to share our knowledge with you
and remain at your disposal for any further questions.
Malte Oellers
- Product Manager
- +49 2154 88999 0
- moellers@pureon.com